Erfan Handoko, Mangasi Alion Marpaung, Zulkarnain Jalil, Adi Rahwanto, Teuku Budi Aulia, Yofentina Iriani, Adayila Muda Mutiara, Ghania Ayu Utami, Juwanda Fernando, Lily Amanda Tarihoran, Sahat Maruli Tua Munthe, Umaisaroh Umaisaroh, Mudrik Alaydrus
To enhance the magnetic and microwave absorbing properties, barium hexaferrite, BaFe12O19, was studied in the x-band (7-13 GHz) frequency range. The BaFe12O19 was prepared as non-magnetized and magnetized samples. The crystal structure, surface morphology, magnetic and microwave absorption of BaFe12O19 were studied with X-ray diffraction (XRD), optical microscope, permagraph and vector network analyzer (VNA), respectively. XRD result showed the formation of M-type hexagonal polycrystalline structure. The hysteresis loop results verified the formation of permanent magnet with high saturation magnetization. The VNA results showed that reflection loss and absorption were - 71.07 dB and 67.96% for magnetized barium hexaferrite, respectively. © Published under licence by IOP Publishing Ltd.
Department of Physics, Universitas Negeri Jakarta, Jalan Rawamangun Muka, Jakarta, 13220, Indonesia; Department of Civil Engineering, Syiah Kuala University, Banda Aceh, 23111, Indonesia; Department of Physics, Universitas Negeri Malang, Jl. Semarang 5, Malang, 65145, Indonesia; Department of Physics, Faculty of Matematics and Natural Sciences, Sebelas Maret University, 57126, Indonesia; Department of Electrical Engineering, Universitas Mercu Buana, Jalan Meruya Selatan No.1, Jakarta, 11650, Indonesia