Hartatiek, Yudyanto, E.K. Velayati, Y.A. Hariyanto, N. Hidayat, A. Taufiq, M. Diantoro
In this research, β-TCP composited with zirconia at different compositions were fabricated via solid-state reaction method. β -TCP was produced from eggshell. The crystal structure of the as-prepared samples was characterized using X-ray diffractometer (X-RD). Meanwhile, elemental mapping and the microstructural characteristics of the samples were characterized by scanning electron microscopy (SEM). A Vickers hardness test was performed to investigate the hardness properties. In addition, the porosity and the electrical conductivity of the sample were also analyzed. The XRD data showed that β-TCP was successfully synthesized from the eggshell. Based on Vickers hardness test results presented the sample with 40:60 wt% composition has a higher hardness that supported by SEM characterization that is homogeneous. Furthermore, the electrical conductivity with the highest value of 0.05470 (S•cm-1) showed by the sample with 30:70 wt% composition. © Published under licence by IOP Publishing Ltd.
Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Malang, Jl. Semarang 5, Malang, 65145, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock